These parts play a part in cooling down the cooling water and engine heat through the influx of external air, and also protecting the inside from fragments

Product packaging and Shipping conditions

20kgs/Pallet or Carton Box

Download related information

Product info

Business Field Market Manufacturer Department
Composites Mobility KoreaComposite R&D Center

product description

SMC material

  • SMC material has excellent thermal vulcanizing ability, excellent strength, and electrical insulation characteristics.
  • Seat SMC is a press molding material on a sheet with excellent moldability by impregnating unsaturated polyester resin with reinforcing material, filler, mold release agent, pigment, catalyst etc. and increasing viscosity by chemical. Thus, SMC can be adjusted according to the desired physical properties of the product because its change range of strength and various physical properties is wide according to the impregnation and arrangement of glass, which is a reinforcing material, and the filler.
Test item Test method Unit Category Test result Requirements
Gloss MS 655-08 : 5th 1 88.4
Water resistance MS 655-08 : 5차 1 Exterior No discoloration, change of color, cracking, gloss degradation on the coating film No discoloration, change of color, cracking,gloss degradation, on the coating film,andAdhesive is M-1, 0 ~Within M~2.5 Color difference(△E*) : 2.0 or less /Gray scale(Grade) : Grade 3 or more
Adhesive(Grade) M-1.0
Color difference(△E*) 0.47
Gray scale(Grade) 4-5
Scratch resistance MS 655-08 : 5th Grade 1 4 3.5 or more
Moisture resistance MS 655-08 : 5th 1 Exterior No discoloration, change of color, cracking, gloss degradation on the coating film No discoloration, change of color, cracking,gloss degradation, on the coating film,andAdhesive is M-1, 0 ~Within M~2.5 /Color difference(△E*) : 2.0 or less /Gray scale(grade) : Grade 3 or more
Adhesive(Grade) M-1.0
Color difference(△E*) 0.42
Gray scale(Grade) 4-5
Alkali resistance MS 655-08 : 5차 1 Exterior No discoloration, change of color, cracking, gloss degradation on the coating film There should be no discoloration, change of color, cracking,gloss degradation, and substrate exposure on the coating film /Gray scale(grade) : Grade 3 or more
Gray scale(Grade) 4-5
Salt Spray Resistance MS 655-08 : 5th 1 Exterior No discoloration, change of color, cracking, gloss degradation on the coating film No discoloration, change of color, cracking,gloss degradation on the coating film,and Adhesive is M-1, 0 ~Within M~2.5 /Color difference(△E*) : 2.0 or less /Gray scale(grade) : Grade 3 or more
Adhesive(Grade) M-1.0
Color difference(△E*) 0.29
Gray scale(Grade) 4-5
PencilHardness MS 655-08 : 5th 1 H or more HB or more

< Material report >

Test item Unit SampleCategory Results Test method
Loss ignition % 29.6 ASTM D2584-11
Specific Gravity((23/23)℃) 1.88 ASTM D792-13(A Method))
Tensile strength MPa 111 ASTM D638-14(*)
Flexural strength MPa 208 ASTM D790-17(**)
Flexural modulus of elasticity GPa 10.5 ASTM D790-17(**)
Izod Impact Strength J/m 1.203(P) ASTM D256-10e1(A Method)
Izod Impact Strength(~40℃) J/m 1.484(P) ASTM D256-10e1(A Method)(***)
Load deformation temperature(1.82MPa) Not measurable(****) ASTM D648-16(B Method)
Absorption rate (24h Immersion) % 0.47 ASTM D570-98(2010)e1

* Test speed: 5 mm/min, Test surface: Type I / ** Test speed : 1.4 mm/min, Distance Between Supports : 50 mm / *** Status control : (-40 ±2) ℃ X 30 min / **** Specified deformation (0.25 mm) does not occur up to maximum temperature of equipment (300 ° C)

Supply Ability

  • Process: 800T/ 1000T/ 2500T PRESS -> Sanding -> Painting -> AssemblyLead Time : 3 days

Packing & Delivery

    • Packaging Details : 20kgs
    • Lead Time : 3days