REAR GLASS GARNISH

REAR GLASS GARNISH

These parts are attached to the front and rear of a vehicle, and serves to increase design effect, and are used for marking emblems and car model, etc.

Product packaging and Shipping conditions

4kgs/Pallet or Carton Box

Download related information

Product info

Business Field Market Manufacturer Department
Composites Mobility KoreaComposite Advanced Sales & Commercial Team

product description

  • SMC material has excellent thermal vulcanizing ability, excellent strength, and electrical insulation characteristic
  • Seat SMC is a press molding material on a sheet with excellent moldability by impregnating unsaturated polyester resin with reinforcing material, filler, mold release agent, pigment, catalyst etc. and increasing viscosity by chemical. Thus, SMC can be adjusted according to the desired physical properties of the product because its change range of strength and various physical properties is wide according to the impregnation and arrangement of glass, which is a reinforcing material, and the filler.

< Reliability Test >

Test item Test method Unit Category Test result Requirements
Gloss MS 655-08 : 5th 1 88.4
Water resistance MS 655-08 : 5th 1 Exterior No discoloration, change of color, cracking, gloss degradation, on the coating No discoloration, change of color, cracking, gloss degradation, on the coatingfilm, andAdhesive is M-1, 0 ~Within M~2.5 Color difference(△E*) : 2.0 or less /Gray scale(Grade) : Grade 3 or more
Adhesive(Grade) M-1.0
Color difference(△E*) 0.47
Gray scale(Grade) 4-5
Scratch resistance MS 655-08 : 5th Grade 1 4 3.5 or more
Moisture resistance MS 655-08 : 5th 1 Exterior No discoloration, change of color, cracking, gloss degradation, on the coating No discoloration, change of color, cracking, gloss degradation, on the coatingfilm, andAdhesive is M-1, 0 ~Within M~2.5 / Color difference(△E*) : 2.0 or less /Gray scale(Grade : Grade 3 or more
Adhesive(Grade) M-1.0
Color difference(△E*) 0.42
Gray scale(Grade) 4-5
Alkali resistance MS 655-08 : 5th 1 Exterior No discoloration, change of color, cracking, gloss degradation, on the coating There should be no discoloration, change of color, cracking,gloss degradation, and substrate exposure on the coating film /Gray scale(Grade) : Grade 3 or more
Gray scale(Grade) 4-5
Salt Spray Resistance MS 655-08 : 5th 1 Exterior No discoloration, change of color, cracking, gloss degradation, on the coating No discoloration, change of color, cracking, gloss degradation, on the coatingfilm, andAdhesive is M-1, 0 ~Within M~2.5 / Color difference(△E*) : 2.0 or less /Gray scale(Grade) : Grade 3 or more
Adhesive(Grade) M-1.0
Color difference(△E*) 0.29
Gray scale(Grade) 4-5
Pencil Hardness MS 655-08 : 5th 1 H or more HB or more

< Material report >

Test item Unit SampleCategory Results Test method
Loss ignition % 29.6 ASTM D2584-11
Specific Gravity((23/23)℃) 1.88 ASTM D792-13(A Method))
Tensile strength MPa 111 ASTM D638-14(*)
Flexural strength MPa 208 ASTM D790-17(**)
Flexural modulus of elasticity GPa 10.5 ASTM D790-17(**)
Izod Impact Strength J/m 1.203(P) ASTM D256-10e1(A Method)
Izod Impact Strength(~40℃) J/m 1.484(P) ASTM D256-10e1(A Method)(***)
Load deformation temperature(1.82MPa) measurable(****) ASTM D648-16(B Method))
Absorption rate(24h Immersion) % 0.47 ASTM D570-98(2010)e1

* Test speed : 5 mm/min, Test surface : Type I / ** Test speed : 1.4 mm/min, Distance Between Supports : 50 mm / *** Status control : (-40 ±2) ℃ X 30 min / **** Specified deformation (0.25 mm) does not occur up to maximum temperature of equipment (300 ° C)

Supply Ability

  • Process: 800T/ 1000T/ 2500T PRESS -> Sanding -> Painting -> AssemblyLead Time : 2 days

Packing & Delivery

    • Packaging Details : 4kgs