Agricultural Hood
Agricultural Hood
It is a cover of a tractor, and it is manufactured in All-in-One(1 piece), or Detachable(4 pieces) using the RIM(DCPD), SMC(UP+GF30%) method. Major Client Company: Daedong Co.,Ltd. TYM Tractors, ISEKI
Product packaging and Shipping conditions
Steel Pallet or Wooden Box Contact Supplier, FOB,CIF,CFR terms.Download related information
Product info
| Business Field | Market | Manufacturer | Department |
|---|---|---|---|
| Composites | Mobility | KoreaComposite | Equipment Marketing & Sales Team |
product description
FINEpol 330 SYSTEM is CO2 Foaming Polyurethane foam undiluted solution which was developed with the aim to insulate high-density LNG Pipe and Support Beam.
FINEpol SYSTEM makes foam and does processing by mixing MDI and Premixed polyol.
With B solution(Premixed polyol) and A solution(Polymeric MDI) mixed through an exclusive foam-making equipment, the mixed solution is sprayed.
After the mixed solution is injected into a fixed frame based on the injection method, the solution is hardened, displaying the highest density among the insulators.
A suited insulation product is selected according to construction places, required property, work and equipment condition, and as regards detailed information and application method about each product, you can get them through this company-affiliated research institute.
As regards the change of product property and cause of defects consequent on the temperature, humidity and working conditions at a construction site, our company is offering constructible technologies under the optimum condition on the basis of technical skills built up for many years.
FINEpol 820S SYSTEM is Polyurethane foam undiluted solution which was developed for an adhesive of EPS/Glass-wool Pane.
FINEpol SYSTEM makes foam and does processing by mixing MDI and Premiexd polyol.
FINEpol 820S consists of a total of 6 sorts of products consequent on reaction time (12, 14, 16, 18, 20, 22 seconds).
B solution (Premixed polyol) and A solution (Polymeric MDI) are mixed through an exclusive foam-making equipment, and then the mixed solution is sprayed.
As PU adhesive system for Sandwich Panel which is used for adhesion with EPS, Glass-wool andiron plates, FINEpol 820S SYSTEM retains excellent adhesive strength and outstanding durability even under the long-term outside adverse conditions.
A suited insulation product is selected according to construction places, required property, work and equipment condition, and as regards detailed information and application method about each product, you can get them through this company-affiliated research institute.
As regards the change of product property and cause of defects consequent on the temperature, humidity and working conditions at a construction site, our company is offering constructible technologies under the optimum condition on the basis of technical skills built up for many years.
1. About RIM Method
- RIM Method is Mixing liquid raw materials of low molecular weight having more than two sorts of reactivity through the use of DCPD (Dicyclopentadiene) raw materials, and then inject the mixed liquid raw materials into a mold, finally manufacturing the wanted object through polymerization of the raw materials in a mold. - DCPD(Dicyclopentadiene) is a substance contained in C5 Fraction obtained as a by-product in the Naphtha distillation process, and this substance, as a thermosetting resin, can form a product of large, complicated shape in a short time.
2. Characteristics of the RIM Method
1) Lightening: It’ possible to implement lightening of shaped articles with low specific gravity(1.03) along with fuel efficiency improvement, contribution to reduction in exhaust gas emissions, and high assembly efficiency.
2) Shock Resistance: Intensification of shock resistance without glass fiber reinforcement (It has proper toughness, and it is recovered even when anomalous strength is added.)
3) Low Temperature Characteristics: The RIM Method shows only a few changes in impact resistance strength even down to -40℃.
4) High Degree of Freedom of Design – Easy to manufacture large goods and complicated shape using materials with low viscosity
5) Productivity: It doesn’t need a releasing agent, and post-cure, and its reaction time is short. (Injection Time: 15~20 seconds, Cure Time; about 60~90 seconds, Basic Cycle Time: 10 min.)
6) Corrosion Resistance: It doesn’t rust even when painting is peeled off by external shocks 7) Painting Adhesiveness: Good Paint Adhesiveness
3. RIM Molding Mimetic Diagram
4. P_DCPD Material Report
| Item | Temperature | Unit | DCPD (Metton T02) | |
| Test Standard | Property | |||
| Specific Gravity | 23 degrees | - | JIS K7112 | 1.03 |
| Tensile Strength | 23 degrees | MPa | JIS K7113 | 45 |
| Tensile Modulus | 23도 | GPa<0/td> | JIS K7113 | 1.9 |
| Bending Strength | 23 degrees | MPa | JIS K7171 | 69 |
| Flexion Elasicity | 23 degrees | GPa | JIS K7171 | 1.8 |
| lzod Impact Resistance Strength | 23 degrees | J/cm | JIS K7110 | 3.9 |
| -30 degrees | JIS K7110 | 2.1 | ||
| Heat Deflection Temperature | - | ℃(18.5kg㎠) | JIS K7207 | 110 |
| Linear coefficient of expansion | - | 1/K | JIS K7197 | 8.7x10-5 |
| Molding Shrinkage rate | - | - | - | 0.009 |
Supply Ability
- 1.Retained Equipment/Vertical type 2set,
application
Contacts
Contact supplier